Compositions and magnetic properties of CoO/Co/Ge(111) films

Jyh Shen Tsay*, Po Ching Chuang, Cheng Hsun Tony Chang, Yeong Der Yao

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

2 引文 斯高帕斯(Scopus)

摘要

On the top of Co/Ge(111) films, cobalt oxides are prepared by evaporating Co atoms in an oxygen atmosphere. Depth profiling measurements show a layered structure of a pure Co layer covered by a CoO overlayer. As the CoO thickness increases, the Auger intensity ratio of O KL2L2 and Co L3M45M45 Auger signals increases until reaching a saturated value which shows a CoO layer with a concentration ratio of Co and O close to 1:1. After introduction of CoO overlayers on Co/Ge(111), hysteresis occurs in the longitudinal configuration and CoO/Co/Ge(111) exhibits in-plane anisotropy. A slight reduction of the Kerr intensity occurs due to the oxidation of cobalt at the CoO/Co interface while an enhanced coercive force is observed owing to the imperfection introduced by oxygen to impede the magnetization reversal. Under conditions of cooling in a magnetic field, exchange bias field increases as the sample temperature decreases resulting from the formation of an antiferromagnetic/ferromagnetic interface.

原文英語
文章編號2275992
期刊IEEE Transactions on Magnetics
50
發行號1
DOIs
出版狀態已發佈 - 2014 一月

ASJC Scopus subject areas

  • 電子、光磁材料
  • 電氣與電子工程

指紋

深入研究「Compositions and magnetic properties of CoO/Co/Ge(111) films」主題。共同形成了獨特的指紋。

引用此