Comparisons of magnetic defects and coercive forces for Co/Si(100) and Co/rubrene/Si(100)

Yen Wei Jhou, Cheng Hsun Tony Chang, Siang Yu Sie, Chun Kai Yang, Chen Yuan Hsieh, Chih Ming Lin, Jyh Shen Tsay*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Spintronics can add new functionalities to electronic devices by utilizing the spin degree of freedom of electrons. Investigating magnetic defects is crucial for the performance of spintronics devices. However, the effects of magnetic defects that are introduced by the presence of organic materials on their magnetic properties remain unclear. Herein, we report on a novel method using rubrene combined with Kerr microscopy that enables quantitative and direct measurements of magnetic defect density. For Co/Si(100) at a magnetic field near the coercivity value, Kerr microscopy images show a dark image with some magnetic defects. Because of domain wall motion, small patches gradually change the contrast. These magnetic defects are immovable at different magnetic fields and serve as pinning sites for domain wall motion. Experimental evidence shows that coercive force can be reduced by controlling the magnetic defect density by introducing small amounts of rubrene into the films. Furthermore, direct quantitative measurements of magnetic defects show both a one-dimensional bowing of domain walls and strong defect-domain wall interactions in the films. Based on these findings, we propose a viable strategy for reducing the coercive force of Co/Si(100) by controlling the magnetic defect density and this new information promises to be valuable for future applications of spintronics devices.

原文英語
頁(從 - 到)14900-14909
頁數10
期刊Physical Chemistry Chemical Physics
22
發行號26
DOIs
出版狀態已發佈 - 2020 7月 14

ASJC Scopus subject areas

  • 物理與天文學 (全部)
  • 物理與理論化學

指紋

深入研究「Comparisons of magnetic defects and coercive forces for Co/Si(100) and Co/rubrene/Si(100)」主題。共同形成了獨特的指紋。

引用此