Characterization of magnetoimpedance on polycrystalline and amorphous chromium oxides bilayered thin films

C. M. Fu*, C. J. Lai, H. S. Hsu, Y. C. Chao, J. C.A. Huang, C. C. Wu, S. G. Shyu

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

6 引文 斯高帕斯(Scopus)

摘要

The impedance of chemical vapor deposited CrO 2 and Cr 2O 3 bilayered thin films, composed of polycrystalline and amorphous structure, have been systematically studied in function of frequency and temperature. In the polycrystalline-CrO 2/amorphous-Cr 2O 3 bilayer, the real part of impedance at low frequency (f<300kHz) demonstrates a sharp transition at temperature around 330 K, with a specific feature of positive temperature coefficient, similar to the variation of dc resistance occurs at ferroelectric-paraelectric transition in the BaTiO 3 ceramics. In contrast, the imaginary part of impedance, at frequency f>300kHz, shows a characteristic of negative temperature coefficient. Further analysis of the frequency dependence of the impedance shows the contribution from the dynamics of both the dielectric and magnetic dipoles in the layers. Comparison of polycrystalline-CrO 2 and amorphous-Cr 2O 3 single layer with the CrO 2/Cr 2O 3 bilayer is discussed.

原文英語
頁(從 - 到)7143-7145
頁數3
期刊Journal of Applied Physics
91
發行號10 I
DOIs
出版狀態已發佈 - 2002 五月 15
對外發佈

ASJC Scopus subject areas

  • 物理與天文學 (全部)

指紋

深入研究「Characterization of magnetoimpedance on polycrystalline and amorphous chromium oxides bilayered thin films」主題。共同形成了獨特的指紋。

引用此