Changes in the Magnetic Anisotropy of Co Thin Films on Pt(111) Capped by Ag Overlayers

C. W. Su, H. Y. Ho, C. S. Shern, R. H. Chen

研究成果: 雜誌貢獻文章

1 引文 (Scopus)

摘要

Two unusual magnetic properties were observed when Co ultrathin films on Pt(111) were capped with Ag overlayers. The perpendicular magnetic anisotropy was significantly enhanced after annealing at high temperatures, and the spin reorientation transition (SRT) could be induced by the Ag overlayers. The perpendicular magnetic anisotropy of 1 ML Ag/1-3.5 monolayers (ML) Co/Pt(111) was enhanced dramatically after Co-Pt alloy formation. The easy axis of the magnetization was reoriented from the in-plane direction to the out-of-plane direction, when Ag overlayers were deposited on 3.5-7 ML Co/Pt(111). The possible mechanisms for the magnetic anisotropy enhancement and the SRT are discussed.

原文英語
頁(從 - 到)519-527
頁數9
期刊Chinese Journal of Physics
41
發行號5
出版狀態已發佈 - 2003 十月 1

指紋

anisotropy
retraining
thin films
magnetic properties
magnetization
annealing
augmentation

ASJC Scopus subject areas

  • Physics and Astronomy(all)

引用此文

Changes in the Magnetic Anisotropy of Co Thin Films on Pt(111) Capped by Ag Overlayers. / Su, C. W.; Ho, H. Y.; Shern, C. S.; Chen, R. H.

於: Chinese Journal of Physics, 卷 41, 編號 5, 01.10.2003, p. 519-527.

研究成果: 雜誌貢獻文章

@article{a10872061dc94152ae1031e41b2305f2,
title = "Changes in the Magnetic Anisotropy of Co Thin Films on Pt(111) Capped by Ag Overlayers",
abstract = "Two unusual magnetic properties were observed when Co ultrathin films on Pt(111) were capped with Ag overlayers. The perpendicular magnetic anisotropy was significantly enhanced after annealing at high temperatures, and the spin reorientation transition (SRT) could be induced by the Ag overlayers. The perpendicular magnetic anisotropy of 1 ML Ag/1-3.5 monolayers (ML) Co/Pt(111) was enhanced dramatically after Co-Pt alloy formation. The easy axis of the magnetization was reoriented from the in-plane direction to the out-of-plane direction, when Ag overlayers were deposited on 3.5-7 ML Co/Pt(111). The possible mechanisms for the magnetic anisotropy enhancement and the SRT are discussed.",
author = "Su, {C. W.} and Ho, {H. Y.} and Shern, {C. S.} and Chen, {R. H.}",
year = "2003",
month = "10",
day = "1",
language = "English",
volume = "41",
pages = "519--527",
journal = "Chinese Journal of Physics",
issn = "0577-9073",
publisher = "Physical Society of the Republic of China",
number = "5",

}

TY - JOUR

T1 - Changes in the Magnetic Anisotropy of Co Thin Films on Pt(111) Capped by Ag Overlayers

AU - Su, C. W.

AU - Ho, H. Y.

AU - Shern, C. S.

AU - Chen, R. H.

PY - 2003/10/1

Y1 - 2003/10/1

N2 - Two unusual magnetic properties were observed when Co ultrathin films on Pt(111) were capped with Ag overlayers. The perpendicular magnetic anisotropy was significantly enhanced after annealing at high temperatures, and the spin reorientation transition (SRT) could be induced by the Ag overlayers. The perpendicular magnetic anisotropy of 1 ML Ag/1-3.5 monolayers (ML) Co/Pt(111) was enhanced dramatically after Co-Pt alloy formation. The easy axis of the magnetization was reoriented from the in-plane direction to the out-of-plane direction, when Ag overlayers were deposited on 3.5-7 ML Co/Pt(111). The possible mechanisms for the magnetic anisotropy enhancement and the SRT are discussed.

AB - Two unusual magnetic properties were observed when Co ultrathin films on Pt(111) were capped with Ag overlayers. The perpendicular magnetic anisotropy was significantly enhanced after annealing at high temperatures, and the spin reorientation transition (SRT) could be induced by the Ag overlayers. The perpendicular magnetic anisotropy of 1 ML Ag/1-3.5 monolayers (ML) Co/Pt(111) was enhanced dramatically after Co-Pt alloy formation. The easy axis of the magnetization was reoriented from the in-plane direction to the out-of-plane direction, when Ag overlayers were deposited on 3.5-7 ML Co/Pt(111). The possible mechanisms for the magnetic anisotropy enhancement and the SRT are discussed.

UR - http://www.scopus.com/inward/record.url?scp=0346331410&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0346331410&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0346331410

VL - 41

SP - 519

EP - 527

JO - Chinese Journal of Physics

JF - Chinese Journal of Physics

SN - 0577-9073

IS - 5

ER -