Carbon dioxide enrichment pebax/mof composite membrane for co2 separation

Po Hsiang Tang, Pamela Berilyn So, Wa Hua Li, Zi You Hui, Chien Chieh Hu*, Chia Her Lin

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Zeolitic imidazole framework (ZIF-8) was incorporated into poly(ether-block-amide) (Pebax-1657) in differing ratios to prepare mixed matrix membranes (MMMs) for gas separation. As ZIF-8 loading is increased, gas separation selectivity also gradually increases. For economic consid-erations, the proportion of the increase in selectivity to the amount of MOF loaded per unit was calculated. The results show that mixing 5% MOF gives the best unit performance. With this, a va-riety of MOFs (UiO-66, UiO-66-NH2, A520, MIL-68(Al) and MIL-100(Fe)) were mixed with PEBAX at 5 loading to prepare MMMs. In this work, metal-organic frameworks (MOFs) were processed using the dry-free method, where in the synthesized MOF was not dried prior to incorporation. The gas separation performance test carried out shows the highest separation performance was exhib-ited by P-UiO-66, wherein the CO2/N2 gas selectivity was 85.94, and the permeability was 189.77 (Barrer), which was higher than Robeson’s Upper bound in 2008, and obtained a high permeability and selectivity among mixed matrix membranes. In the preparation of high quality MMMs for gas separation, details regarding the interface phenomenon were assessed.

原文英語
文章編號404
期刊Membranes
11
發行號6
DOIs
出版狀態已發佈 - 2021 六月

ASJC Scopus subject areas

  • 化學工程(雜項)
  • 製程化學與技術
  • 篩選和分離

指紋

深入研究「Carbon dioxide enrichment pebax/mof composite membrane for co2 separation」主題。共同形成了獨特的指紋。

引用此