Atomic exchange and magnetic properties of Co/Ag/Pt(111)

C. L. Tzeng, C. W. Su, H. Y. Ho, C. S. Shern

研究成果: 雜誌貢獻會議論文同行評審

摘要

The structure of Co ultrathin films deposited on 1 ML Ag/Pt(111) surface was studied by Auger electron spectroscopy (AES), and low-energy electron diffraction (LEED). The atomic exchange between Ag and Co occurs at a high temperature annealing. The magnetic property was studied by a magneto-optic Kerr effect (MOKE). The easy axis of the magnetization of Co deposited on 1 ML Ag/Pt(111) switches from the out-of-plane to the in-plane direction when the coverage of Co is larger than 2 ML. The easy axis can change back to the out-of-plane direction after a high temperature annealing for 2-7 ML Co/1 ML Ag/Pt(111). The study of the interface structure shows that the spin reorientation transition occurs when the atomic exchange between Ag and Co occurs. Further annealing at higher temperatures, the perpendicular magnetic anisotropy significantly enhances. The enhancement of the perpendicular magnetic anisotropy is due to the formation of Co-Pt alloy after the atomic exchange between Co and Ag. The possible mechanisms for the spin reorientation transition and the enhancement in the perpendicular magnetic anisotropy are discussed.

原文英語
頁(從 - 到)82-85
頁數4
期刊Thin Solid Films
459
發行號1-2
DOIs
出版狀態已發佈 - 2004 七月 1
事件Proceedings of the Eight European Vacuum Congress Berlin 2003 - Berlin, 德国
持續時間: 2004 六月 232004 六月 26

ASJC Scopus subject areas

  • 電子、光磁材料
  • 表面和介面
  • 表面、塗料和薄膜
  • 金屬和合金
  • 材料化學

指紋

深入研究「Atomic exchange and magnetic properties of Co/Ag/Pt(111)」主題。共同形成了獨特的指紋。

引用此