Array of CdSe QD-sensitized ZnO nanorods serves as photoanode for water splitting

N. Chouhan*, C. L. Yeh, S. F. Hu, J. H. Huang, C. W. Tsai, R. S. Liu, W. S. Chang, K. H. Chen

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

37 引文 斯高帕斯(Scopus)

摘要

Aqueous chemically grown ZnO nanorods (NRs) arrays were sensitized by CdSe quantum dots (QDs) and were investigated as photoanode for photoelectrochemical water splitting under visible light (>420 nm) illumination. Significant enhancement of the factors 1.6 and 6 was observed for CdSe (QD)-sensitized nonannealed and annealed samples of ZnO NRs over pristine ZnO NRs arrays, respectively. The highest photocurrent density of 2.48 mA/ cm2 was registered for the annealed CdSe (QD)/ZnO (NR) arrays films at zero applied voltage and 100 mW/ cm2 (AM 1.5 G, Air Mass 1.5 Global) power density and their corresponding photocurrent density for pristine ZnO NR array was recorded as 0.41 mA/ cm2.

原文英語
頁(從 - 到)B1430-B1433
期刊Journal of the Electrochemical Society
157
發行號10
DOIs
出版狀態已發佈 - 2010

ASJC Scopus subject areas

  • 電子、光磁材料
  • 可再生能源、永續發展與環境
  • 表面、塗料和薄膜
  • 電化學
  • 材料化學

指紋

深入研究「Array of CdSe QD-sensitized ZnO nanorods serves as photoanode for water splitting」主題。共同形成了獨特的指紋。

引用此