Anomalous high temperature electrical behaviors in Bi2Sr2CaCu2Oy oxides

H. E. Horng, T. H. Lu, S. T. Ho, H. C. Yang

    研究成果: 雜誌貢獻文章同行評審


    The high temperature resistivity (27 - 900 °C) and the x-ray diffraction (27 - 500 °C) have been measured to investigate the anomalous transport behaviors in 90 K Bi2Sr2CaCu2Oy (BSCCO) oxides. A very sharp peak in the high temperature resistivity measurement was observed to occur at a specific temperature Tp as the BSCCO samples were exposed to various gas environments. These specific temperatures are at 275 °C, 389 °C and 450 °C respectively for BSCCO samples in the oxygen (1 atm), vacuum (1 mtorr) and the flowing helium (1 atm) environments. No significant decomposition was detected by the powder x-ray diffraction at temperatures near Tp ± 100 °C. The x-ray diffraction data suggest that the change in the lattice parameters possibly causes the sharp peak of the high temperature resistivity data; which therefore affects the superconducting transition temperature of BSCCO samples.

    頁(從 - 到)2201-2202
    期刊Physica B: Physics of Condensed Matter
    發行號PART 2
    出版狀態已發佈 - 1994 二月 2

    ASJC Scopus subject areas

    • Electronic, Optical and Magnetic Materials
    • Condensed Matter Physics
    • Electrical and Electronic Engineering

    指紋 深入研究「Anomalous high temperature electrical behaviors in Bi<sub>2</sub>Sr<sub>2</sub>CaCu<sub>2</sub>O<sub>y</sub> oxides」主題。共同形成了獨特的指紋。