An integrated cobalt disulfide (CoS2) co-catalyst passivation layer on silicon microwires for photoelectrochemical hydrogen evolution

Chih Jung Chen, Po Tzu Chen, Mrinmoyee Basu, Kai Chih Yang, Ying Rui Lu, Chung Li Dong, Chong Geng Ma, Chin Chang Shen, Shu Fen Hu*, Ru Shi Liu

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

49 引文 斯高帕斯(Scopus)

摘要

An integrated cobalt disulfide (CoS2) co-catalyst passivation layer on Si microwires (MWs) was used as a photocathode for solar hydrogen evolution. Si MWs were prepared by photolithography and dry etching techniques. The CoS2-Si photocathodes were subsequently prepared by chemical deposition and thermal sulfidation of the Co(OH)2 outer shell. The optimized onset potential and photocurrent of the CoS2-Si electrode were 0.248 V and -3.22 mA cm-2 (at 0 V), respectively. The best photocatalytic activity of the CoS2-Si electrode resulted from lower charge transfer resistances among the photoabsorber, co-catalyst, and redox couples in the electrolyte. X-ray absorption near edge structure was conducted to investigate the unoccupied electronic states of the CoS2 layer. We propose that more vacancies in the S-3p unoccupied states of the CoS2-Si electrode were present with a lower negative charge of S22- to form weaker S-H bond strength, promoting water splitting efficiency. Moreover, the CoS2 co-catalyst that completely covered underlying Si MWs served as a passivation layer to prevent oxidation and reduce degradation during photoelectrochemical measurements. Therefore, the optimal CoS2-Si electrode maintained the photocurrent at about -3 mA cm-2 (at 0 V) for 9 h, and its hydrogen generation rate was approximately 0.833 μmol min-1.

原文英語
頁(從 - 到)23466-23476
頁數11
期刊Journal of Materials Chemistry A
3
發行號46
DOIs
出版狀態已發佈 - 2015

ASJC Scopus subject areas

  • 化學 (全部)
  • 可再生能源、永續發展與環境
  • 材料科學(全部)

指紋

深入研究「An integrated cobalt disulfide (CoS<sub>2</sub>) co-catalyst passivation layer on silicon microwires for photoelectrochemical hydrogen evolution」主題。共同形成了獨特的指紋。

引用此