An analysis and research on the transmission ratio of dye sensitized solar cell photoelectrodes by using different etching process

Chin Guo Kuo, Cheng Fu Yang, Mu Jung Kao*, Wen Pin Weng, Chi Cheng Chang, Lih Ren Hwang, Jian Lan Nil

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

5 引文 斯高帕斯(Scopus)

摘要

Classical photoelectrodes for Dye Sensitized Solar Cells (DSSCs) were fabricated by using the electrochemical method on the titanium (Ti) template, for that the fabrication process would influence the characteristics of the DSSCs. In this study, at first three different methods were used to etch Ti templates from 10 to 17 min, (1) polishing-chemical etching: Ti template was annealed at 450°C for 1 h, abraded using number 80 to 1500 SiC sheet, and then etched in a solution of 5% HF + 95% H; (2) electrochemical polishing-chemical etching: Ti template was annealed at 450°C for 1 h, electrolytic polishing with 42% CHH + 5% HClO+ 53% HOCHHCsolution, and the chemical-etching in a solution of 5% HF + 95% H; (3) chemical etching: Ti template was etched in a solution of 5% HF + 95% H and annealed at 450°C for 1 h. When the etching time was changed from 10 to 17 min, the thicknesses of Ti templates decreased from 75.3 m to 14.8 m, depending on the etching method. After etching process, the TiOnanotube arrays were fabricated as the photoelectrode of DSSCs by electrochemical process, in which the Ti as anode and platinum (Pt) as cathode. The electrolyte solution included COH) NH, and deionized water. After annealing the grown TiOnanotube arrays at 450°C for 3 h, we would show that the etching process had large effect on the structure and transmittance ratio of the TiOnanotube arrays.

原文英語
文章編號151973
期刊International Journal of Photoenergy
2013
DOIs
出版狀態已發佈 - 2013

ASJC Scopus subject areas

  • 一般化學
  • 原子與分子物理與光學
  • 可再生能源、永續發展與環境
  • 一般材料科學

指紋

深入研究「An analysis and research on the transmission ratio of dye sensitized solar cell photoelectrodes by using different etching process」主題。共同形成了獨特的指紋。

引用此