An amphoteric hydrogel: Synthesis and application as an internal curing agent of concrete

Xin Yi Liu, Chang Hsiang Huang, Ching Hsiang Zhuang, Kung Chung Hsu*, Chung Ho Huang

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

4 引文 斯高帕斯(Scopus)

摘要

A new crosslinked amphoteric hydrogel (PAC) was synthesized and evaluated as an internal curing agent of concrete. PAC was prepared from acrylamide (AM) and 4-(2-((carboxylatomethyl)dimethylammonio)ethoxy)-4-oxobut-2-enoate (CMD) through free-radical polymerization by using ammonium persulfate (APS) as an initiator and methylene-bisacrylamide (MBA) as a crosslinker. The structure of the prepared polymer was verified by the IR spectra. The effects of the polymerization variables on the swelling capacity of PAC were investigated. The water absorbency of PAC was found to increase with increasing CMD/AM ratio, reach a maximum value, and decrease afterword. Increase of either APS or MBA content decreased the water absorbency. The highest water absorbency of PAC hydrogel (P7) achieved in deionized water, 0.1M NaCl solutions and 0.1M CaCl2 solutions, was 306 g/g, 32 g/g, and 22 g/g, respectively. Compared with a commercial acrylate-based hydrogel 283HA, P7 was less sensitive to the existence of Ca2+ ions in cement pore solutions, and more effective in reducing the cracking tendency of cement pastes. Finally, mortars incorporated with proper amounts of P7 showed smaller drying shrinkage and higher compressive strength than that without hydrogel present.

原文英語
文章編號42175
期刊Journal of Applied Polymer Science
132
發行號26
DOIs
出版狀態已發佈 - 2015 七月 1

ASJC Scopus subject areas

  • 化學 (全部)
  • 表面、塗料和薄膜
  • 聚合物和塑料
  • 材料化學

指紋

深入研究「An amphoteric hydrogel: Synthesis and application as an internal curing agent of concrete」主題。共同形成了獨特的指紋。

引用此