All-Solution-Processed Red and Orange-Red Organic Light-Emitting Diodes with High-Efficiencies: The Effect of Mixed-Host Emissive Layers and Thermal Annealing Treatment

Yu Fan Chang*, Lan Sheng Yang, Hsiao Tso Su, Si Yi Liao, Mu Chun Niu, K. P.O. Mahesh, Chao Hsuan Chen, Yu Chiang Chao, Hsin Fei Meng, Heh Lung Huang, Teng Chih Chao, Meu Rurng Tseng, Chih Wei Luo, Hsiao Wen Zan, Sheng Fu Horng

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

9 引文 斯高帕斯(Scopus)

摘要

The instability of the organic light-emitting diodes (OLEDs) during operation can be attributed to the existence of point defects on the organic layers. In this work, the effect of mixed-host emissive layer and the thermal annealing treatment were investigated to eliminate defects and to boost the device performance. The mixed-host system includes 4,4′,4′′-tri (9-carbazoyl) triphenylamine (TCTA) and 2,7-bis(diphenylphosphoryl)-9, 9′-spirobi[fluorene] (SPPO13). The mixed-host emissive layer with thermal annealing treatment showed low roughness and few pinholes, and the devices fabricated from this emissive layer exhibited high efficiencies, high stabilities, and long lifetimes. The red and orange-red OLEDs exhibited efficiencies of 13.9 cd/A and 24.35 cd/A, respectively. The longest half-lifetime (L0=500 cd/m2) of the red and orange-red OLEDs were 158 h and 180 h, respectively. Efforts were made to solve problems in large-area coating and to reduce the number of defects on in organic layer. Large-active-area (active area=3 cm×4 cm) red phosphorescent OLEDs (PhOLEDs) devices were realized with very high current efficiency up to 9 cd/A.

原文英語
頁(從 - 到)1375-1383
頁數9
期刊ChemPlusChem
84
發行號9
DOIs
出版狀態已發佈 - 2019 9月 1

ASJC Scopus subject areas

  • 一般化學

指紋

深入研究「All-Solution-Processed Red and Orange-Red Organic Light-Emitting Diodes with High-Efficiencies: The Effect of Mixed-Host Emissive Layers and Thermal Annealing Treatment」主題。共同形成了獨特的指紋。

引用此