Abnormal reduction of coercivity on magnetic cobalt-platinum alloy films

C. W. Su*, C. S. Shern

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

摘要

Ultrathin Co-Pt alloy films as substrate were studied by the surface magneto-optical Kerr effect. As the growth of Ni, the films show uniquely high polar Kerr responses without any in-plane signals. The coercivity decreased until the thickness of Ni film was higher than 5 ML. A new surface structure was discovered at 7-10 ML Ni/Co-Pt films by the low-energy electron diffraction. Interestingly, polar Kerr signal and coercivity of the 10 ML Ni/Co-Pt(1 1 1) template film reduced rapidly as Co films were further deposited onto only about 1-2 ML. Then the films show a canted magnetization with a rollback hysteresis in the polar configuration during the growth of Co. Coercivity of the 7 ML Co/Ni/Co-Pt film was found unusually down to almost 100 Oe.The corresponding magic number at around 7 ML of Co in the abnormal reduction of coercivity may be attributed to the cluster formations of Co.

原文英語
頁(從 - 到)e234-e237
期刊Journal of Magnetism and Magnetic Materials
303
發行號2 SPEC. ISS.
DOIs
出版狀態已發佈 - 2006 八月

ASJC Scopus subject areas

  • 電子、光磁材料
  • 凝聚態物理學

指紋

深入研究「Abnormal reduction of coercivity on magnetic cobalt-platinum alloy films」主題。共同形成了獨特的指紋。

引用此