A coral-like film of Ni@NiS with core-shell particles for the counter electrode of an efficient dye-sensitized solar cell

Hui Min Chuang, Chun Ting Li, Min Hsin Yeh, Chuan Pei Lee, R. Vittal, Kuo Chuan Ho*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

63 引文 斯高帕斯(Scopus)

摘要

A coral-like film of nickel@nickel sulfide (Ni@NiS) was obtained on a conducting glass through an electrochemical method, in which the Ni functioned as a template. Three types of Ni thin films were electrodeposited on fluorine-doped tin oxide (FTO) substrates by a pulse current technique at the passed charge densities of 100, 200, and 300 mC cm-2, which rendered custard apple-like, coral-like, and cracked nanostructures, respectively. Subsequently, nickel sulfide films were coated on these Ni films by using a pulse potential technique. Due to the template effect of the Ni films, the composite films of Ni@NiS also assumed the same structures as those of their nickel templates. In each case of the films the particle of the film assumed a core-shell structure. The Ni@NiS coated FTO glasses were used as the counter electrodes for dye-sensitized solar cells (DSSCs). The DSSC with the coral-like Ni@NiS film on its counter electrode exhibits the highest power conversion efficiency (η) of 7.84%, while the DSSC with platinum film on its counter electrode shows an η of 8.11%. The coral-like Ni@NiS film exhibits multiple functions, i.e., large surface area, high conductivity, and great electrocatalytic ability for iodine/triiodine (I-/I3 -) reduction. X-ray photoelectron spectroscopy (XPS), X-ray diffraction pattern (XRD), scanning electron microscopy (SEM), and four-point probe technique were used to characterize the films. The photovoltaic parameters are substantiated using incident photon-to-current conversion efficiency (IPCE) curves, cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and Tafel polarization plots. The IPCE curves were further used to calculate theoretical short-current densities of the cells.

原文英語
頁(從 - 到)5816-5824
頁數9
期刊Journal of Materials Chemistry A
2
發行號16
DOIs
出版狀態已發佈 - 2014 四月 28
對外發佈

ASJC Scopus subject areas

  • 化學 (全部)
  • 可再生能源、永續發展與環境
  • 材料科學(全部)

指紋

深入研究「A coral-like film of Ni@NiS with core-shell particles for the counter electrode of an efficient dye-sensitized solar cell」主題。共同形成了獨特的指紋。

引用此