Welding microstructure and tensile properties of s45c carbon steel

Chin Guo Kuo, Jin Chung Chang, Yi Hsuan Hung, Yen Tien Kang, Chen Yang Kao, Jung Hsuan Chen

Research output: Contribution to journalArticle

Abstract

The purpose of this study was to investigate the dissimilar joint properties of S45C carbon steel with multi-layer and multi-pass welding. We used four weld rods labelled A, B, C, and D to experimentally examine the influence on microstructures. A, B, and C were medium carbon steels while D was stainless steel. The microstructures of joint beads were observed with an optical microscope. The specimens for tensile tests were made in accordance with American Society for Testing and Materials (ASTM) E8M. The experimental results were as follows: (1) Pearlite structures and bainite structures were formed in the welded zone by the weld rods of medium carbon steels. The yield strength and ultimate strength of the specimens were 360 and 460 MPa, respectively. (2) The feature of welded specimen D was close to stainless steel because the stainless steel rod included some Cr and Ni. The yield strength and ultimate strength of specimen D showed increases of 35 and 65% compared to the other specimens. In addition, a ferritic-austenitic stainless steel, known as dual phase stainless steel, was observed in the optical microscope.

Original languageEnglish
Pages (from-to)675-681
Number of pages7
JournalSensors and Materials
Volume30
Issue number3
DOIs
Publication statusPublished - 2018 Jan 1

Fingerprint

tensile properties
Stainless Steel
carbon steels
Tensile properties
welding
Carbon steel
Welding
Stainless steel
stainless steels
microstructure
Microstructure
rods
Yield stress
yield strength
Welds
optical microscopes
Microscopes
Bainite
Pearlite
ferritic stainless steels

Keywords

  • Microstructure
  • S45C carbon steel
  • Tensile property
  • Welding

ASJC Scopus subject areas

  • Instrumentation
  • Materials Science(all)

Cite this

Welding microstructure and tensile properties of s45c carbon steel. / Kuo, Chin Guo; Chang, Jin Chung; Hung, Yi Hsuan; Kang, Yen Tien; Kao, Chen Yang; Chen, Jung Hsuan.

In: Sensors and Materials, Vol. 30, No. 3, 01.01.2018, p. 675-681.

Research output: Contribution to journalArticle

Kuo, Chin Guo ; Chang, Jin Chung ; Hung, Yi Hsuan ; Kang, Yen Tien ; Kao, Chen Yang ; Chen, Jung Hsuan. / Welding microstructure and tensile properties of s45c carbon steel. In: Sensors and Materials. 2018 ; Vol. 30, No. 3. pp. 675-681.
@article{82715020f7004f66a17841a8e0fd1eaa,
title = "Welding microstructure and tensile properties of s45c carbon steel",
abstract = "The purpose of this study was to investigate the dissimilar joint properties of S45C carbon steel with multi-layer and multi-pass welding. We used four weld rods labelled A, B, C, and D to experimentally examine the influence on microstructures. A, B, and C were medium carbon steels while D was stainless steel. The microstructures of joint beads were observed with an optical microscope. The specimens for tensile tests were made in accordance with American Society for Testing and Materials (ASTM) E8M. The experimental results were as follows: (1) Pearlite structures and bainite structures were formed in the welded zone by the weld rods of medium carbon steels. The yield strength and ultimate strength of the specimens were 360 and 460 MPa, respectively. (2) The feature of welded specimen D was close to stainless steel because the stainless steel rod included some Cr and Ni. The yield strength and ultimate strength of specimen D showed increases of 35 and 65{\%} compared to the other specimens. In addition, a ferritic-austenitic stainless steel, known as dual phase stainless steel, was observed in the optical microscope.",
keywords = "Microstructure, S45C carbon steel, Tensile property, Welding",
author = "Kuo, {Chin Guo} and Chang, {Jin Chung} and Hung, {Yi Hsuan} and Kang, {Yen Tien} and Kao, {Chen Yang} and Chen, {Jung Hsuan}",
year = "2018",
month = "1",
day = "1",
doi = "10.18494/SAM.2018.1826",
language = "English",
volume = "30",
pages = "675--681",
journal = "Sensors and Materials",
issn = "0914-4935",
publisher = "M Y U Scientific Publishing Division",
number = "3",

}

TY - JOUR

T1 - Welding microstructure and tensile properties of s45c carbon steel

AU - Kuo, Chin Guo

AU - Chang, Jin Chung

AU - Hung, Yi Hsuan

AU - Kang, Yen Tien

AU - Kao, Chen Yang

AU - Chen, Jung Hsuan

PY - 2018/1/1

Y1 - 2018/1/1

N2 - The purpose of this study was to investigate the dissimilar joint properties of S45C carbon steel with multi-layer and multi-pass welding. We used four weld rods labelled A, B, C, and D to experimentally examine the influence on microstructures. A, B, and C were medium carbon steels while D was stainless steel. The microstructures of joint beads were observed with an optical microscope. The specimens for tensile tests were made in accordance with American Society for Testing and Materials (ASTM) E8M. The experimental results were as follows: (1) Pearlite structures and bainite structures were formed in the welded zone by the weld rods of medium carbon steels. The yield strength and ultimate strength of the specimens were 360 and 460 MPa, respectively. (2) The feature of welded specimen D was close to stainless steel because the stainless steel rod included some Cr and Ni. The yield strength and ultimate strength of specimen D showed increases of 35 and 65% compared to the other specimens. In addition, a ferritic-austenitic stainless steel, known as dual phase stainless steel, was observed in the optical microscope.

AB - The purpose of this study was to investigate the dissimilar joint properties of S45C carbon steel with multi-layer and multi-pass welding. We used four weld rods labelled A, B, C, and D to experimentally examine the influence on microstructures. A, B, and C were medium carbon steels while D was stainless steel. The microstructures of joint beads were observed with an optical microscope. The specimens for tensile tests were made in accordance with American Society for Testing and Materials (ASTM) E8M. The experimental results were as follows: (1) Pearlite structures and bainite structures were formed in the welded zone by the weld rods of medium carbon steels. The yield strength and ultimate strength of the specimens were 360 and 460 MPa, respectively. (2) The feature of welded specimen D was close to stainless steel because the stainless steel rod included some Cr and Ni. The yield strength and ultimate strength of specimen D showed increases of 35 and 65% compared to the other specimens. In addition, a ferritic-austenitic stainless steel, known as dual phase stainless steel, was observed in the optical microscope.

KW - Microstructure

KW - S45C carbon steel

KW - Tensile property

KW - Welding

UR - http://www.scopus.com/inward/record.url?scp=85044439504&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85044439504&partnerID=8YFLogxK

U2 - 10.18494/SAM.2018.1826

DO - 10.18494/SAM.2018.1826

M3 - Article

AN - SCOPUS:85044439504

VL - 30

SP - 675

EP - 681

JO - Sensors and Materials

JF - Sensors and Materials

SN - 0914-4935

IS - 3

ER -