Spontaneous nanostructural island formation and layer-to-island mass transport in Ge layers on Si(111) surfaces

Amal K. Das, S. K. Ghose, B. N. Dev, G. Kuri, T. R. Yang

Research output: Contribution to journalArticle

25 Citations (Scopus)

Abstract

We have deposited Ge on Br-passivated Si(111) surfaces under high vacuum (HV) conditions at room temperature (RT). Ge has grown in a layer-plus-island growth mode. Atomic force microscopy (AFM) measurements on the as-deposited samples show the formation of nanostructural islands. On a 500 °C-annealed sample, the size and the density of islands increase. High resolution X-ray diffraction (HRXRD) and ion channeling experiments show the lack of epitaxial growth. However, Raman spectroscopy measurements show the polycrystallinity of the Ge layer. X-ray reflectivity (XRR) and Raman spectroscopy results show that the Ge/Si interface is sharp for the as-deposited layer and there is no significant intermixing even in the annealed samples. AFM, XRR and Raman spectroscopy results, taken together, indicate mass transport from the Ge layer to Ge islands. The temperature dependence of this mass transfer provides effective activation energy of 0.45±0.04 eV.

Original languageEnglish
Pages (from-to)260-270
Number of pages11
JournalApplied Surface Science
Volume165
Issue number4
DOIs
Publication statusPublished - 2000 Oct 2

    Fingerprint

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Physics and Astronomy(all)
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

Cite this