Signature of lattice defects in far infrared reflectivity of Ba(Mg1/3Ta2/3)O3

T. Shimada, K. Touji, Hsiang Lin Liu, Yuan Tai Tzeng, Chi-Ta Chia, T. Kolodiazhnyi

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

Far infrared reflectivity spectra of Ba(Mg1/3,Ta2/3)O3 prepared at several sintering temperatures were measured, and the eigenfrequencies and damping constants of the TO modes were determined. The reflectivity spectra were fitted with the four-parameter semi-quantum model. The variation in the Eu(OII) at 222 cm-1 and A2u(OII) at 238 cm-1 modes in well ordered ceramics was attributed to the variation in the concentration of the B site defects. It was also found that the change in the oxygen partial pressure of the sintering atmosphere causes a change in the seventh (316 cm-1) and eighth (352 cm-1) modes. We attribute these changes to the oxygen site defect although we cannot evaluate the concentration of this defect at this moment. From the behavior of the damping constants it is suggested that the Ba(Mg1/3Ta2/3)O3 (BMT) attains equilibrium defect density at the heat treatment temperature of more than 1630 °C (120 h).

Original languageEnglish
Pages (from-to)2797-2802
Number of pages6
JournalJournal of the European Ceramic Society
Volume27
Issue number8-9 SPEC. ISS.
DOIs
Publication statusPublished - 2007 Apr 2

Fingerprint

Crystal defects
Infrared radiation
Defects
Sintering
Damping
Oxygen
Defect density
Partial pressure
Heat treatment
Temperature

Keywords

  • Dielectric properties
  • Lattice defects
  • Perovskites
  • Spectroscopy

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

Cite this

Signature of lattice defects in far infrared reflectivity of Ba(Mg1/3Ta2/3)O3. / Shimada, T.; Touji, K.; Liu, Hsiang Lin; Tzeng, Yuan Tai; Chia, Chi-Ta; Kolodiazhnyi, T.

In: Journal of the European Ceramic Society, Vol. 27, No. 8-9 SPEC. ISS., 02.04.2007, p. 2797-2802.

Research output: Contribution to journalArticle

Shimada, T. ; Touji, K. ; Liu, Hsiang Lin ; Tzeng, Yuan Tai ; Chia, Chi-Ta ; Kolodiazhnyi, T. / Signature of lattice defects in far infrared reflectivity of Ba(Mg1/3Ta2/3)O3. In: Journal of the European Ceramic Society. 2007 ; Vol. 27, No. 8-9 SPEC. ISS. pp. 2797-2802.
@article{64dda13a5f8b4d70a7a1162c65294200,
title = "Signature of lattice defects in far infrared reflectivity of Ba(Mg1/3Ta2/3)O3",
abstract = "Far infrared reflectivity spectra of Ba(Mg1/3,Ta2/3)O3 prepared at several sintering temperatures were measured, and the eigenfrequencies and damping constants of the TO modes were determined. The reflectivity spectra were fitted with the four-parameter semi-quantum model. The variation in the Eu(OII) at 222 cm-1 and A2u(OII) at 238 cm-1 modes in well ordered ceramics was attributed to the variation in the concentration of the B site defects. It was also found that the change in the oxygen partial pressure of the sintering atmosphere causes a change in the seventh (316 cm-1) and eighth (352 cm-1) modes. We attribute these changes to the oxygen site defect although we cannot evaluate the concentration of this defect at this moment. From the behavior of the damping constants it is suggested that the Ba(Mg1/3Ta2/3)O3 (BMT) attains equilibrium defect density at the heat treatment temperature of more than 1630 °C (120 h).",
keywords = "Dielectric properties, Lattice defects, Perovskites, Spectroscopy",
author = "T. Shimada and K. Touji and Liu, {Hsiang Lin} and Tzeng, {Yuan Tai} and Chi-Ta Chia and T. Kolodiazhnyi",
year = "2007",
month = "4",
day = "2",
doi = "10.1016/j.jeurceramsoc.2006.11.005",
language = "English",
volume = "27",
pages = "2797--2802",
journal = "Journal of the European Ceramic Society",
issn = "0955-2219",
publisher = "Elsevier BV",
number = "8-9 SPEC. ISS.",

}

TY - JOUR

T1 - Signature of lattice defects in far infrared reflectivity of Ba(Mg1/3Ta2/3)O3

AU - Shimada, T.

AU - Touji, K.

AU - Liu, Hsiang Lin

AU - Tzeng, Yuan Tai

AU - Chia, Chi-Ta

AU - Kolodiazhnyi, T.

PY - 2007/4/2

Y1 - 2007/4/2

N2 - Far infrared reflectivity spectra of Ba(Mg1/3,Ta2/3)O3 prepared at several sintering temperatures were measured, and the eigenfrequencies and damping constants of the TO modes were determined. The reflectivity spectra were fitted with the four-parameter semi-quantum model. The variation in the Eu(OII) at 222 cm-1 and A2u(OII) at 238 cm-1 modes in well ordered ceramics was attributed to the variation in the concentration of the B site defects. It was also found that the change in the oxygen partial pressure of the sintering atmosphere causes a change in the seventh (316 cm-1) and eighth (352 cm-1) modes. We attribute these changes to the oxygen site defect although we cannot evaluate the concentration of this defect at this moment. From the behavior of the damping constants it is suggested that the Ba(Mg1/3Ta2/3)O3 (BMT) attains equilibrium defect density at the heat treatment temperature of more than 1630 °C (120 h).

AB - Far infrared reflectivity spectra of Ba(Mg1/3,Ta2/3)O3 prepared at several sintering temperatures were measured, and the eigenfrequencies and damping constants of the TO modes were determined. The reflectivity spectra were fitted with the four-parameter semi-quantum model. The variation in the Eu(OII) at 222 cm-1 and A2u(OII) at 238 cm-1 modes in well ordered ceramics was attributed to the variation in the concentration of the B site defects. It was also found that the change in the oxygen partial pressure of the sintering atmosphere causes a change in the seventh (316 cm-1) and eighth (352 cm-1) modes. We attribute these changes to the oxygen site defect although we cannot evaluate the concentration of this defect at this moment. From the behavior of the damping constants it is suggested that the Ba(Mg1/3Ta2/3)O3 (BMT) attains equilibrium defect density at the heat treatment temperature of more than 1630 °C (120 h).

KW - Dielectric properties

KW - Lattice defects

KW - Perovskites

KW - Spectroscopy

UR - http://www.scopus.com/inward/record.url?scp=33947643713&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33947643713&partnerID=8YFLogxK

U2 - 10.1016/j.jeurceramsoc.2006.11.005

DO - 10.1016/j.jeurceramsoc.2006.11.005

M3 - Article

AN - SCOPUS:33947643713

VL - 27

SP - 2797

EP - 2802

JO - Journal of the European Ceramic Society

JF - Journal of the European Ceramic Society

SN - 0955-2219

IS - 8-9 SPEC. ISS.

ER -