Organic/metal interface-modulated magnetism in [Fe/C60]3 multilayers and Fe-C60 composites

Chuan Che Hsu, Kai Lin Hsu, Po Chun Chang, Shi Yu Liu, Chien Chen Hsu, Wen Chin Lin

Research output: Contribution to journalArticlepeer-review

6 Citations (Scopus)


Because of the expected long spin-transport length of organic materials, the magnetic metal/organic interface is crucial to the application of organic spintronics. In this study, [Fe/C60]3 multilayers were fabricated for the investigation of C60-mediated magnetic interlayer coupling. [Fe/C60]3 thin films were characterized using the magneto-optical Kerr effect, transmission electron microscopy, Raman spectroscopy, and x-ray photoelectron spectroscopy (XPS). The thin films revealed in-plane magnetic anisotropy, and the magnetic coercivity (Hc) drastically decreased from 6-8 mT to 0.5 mT with the increase of C60 thickness from 0.1 nm to 5 nm. The insertion of the C60 layer considerably reduced Hc because a thickness greater than 1 nm of the C60 layer is sufficient for blocking magnetic exchange coupling between Fe layers. In addition, post-annealing increased Hc because of Fe inter-diffusion, which promotes magnetic exchange coupling and further Fe-C bonding, as confirmed by a comparative study of XPS C-spectra. The thermally triggered inter-diffusion between Fe and C60 layers turned the multilayers into a mixed composite film and thus caused magnetic variation. Annealing time and temperature can be used as control parameters for the tuning of magnetism in Fe-C60 composites.

Original languageEnglish
Article number325701
Issue number32
Publication statusPublished - 2020 Aug 7

ASJC Scopus subject areas

  • Bioengineering
  • General Chemistry
  • General Materials Science
  • Mechanics of Materials
  • Mechanical Engineering
  • Electrical and Electronic Engineering


Dive into the research topics of 'Organic/metal interface-modulated magnetism in [Fe/C60]3 multilayers and Fe-C60 composites'. Together they form a unique fingerprint.

Cite this