Dielectric properties of ultra-low sintering temperature Al2O3-BBSZ glass composite

Ceramic composites of B₂O₃-Bi₂O₃-SiO₂-ZnO (BBSZ) glass mixed with Al₂O₃ (10-50 vol%) were sintered at 450°C, and their microstructural and dielectric properties investigated. Dense structures were obtained when the Al₂O₃ content was lower than 30 vol%. Raman, XRD, and FESEM showed the existence of a secondary phase, Bi₂₄Si₂O₄₀, in all samples. The dielectric properties of the composite with 30 vol% addition of Al₂O₃ showed good dielectric properties with ε_r of 14.8 and 20.8 and 32.5 at 100 kHz and 100 MHz and 1 GHz, respectively. The tanδ values at the same frequencies were 0.004 and 0.006 and 0.016. The results show that BBSZ glass with different amounts of Al₂O₃ exhibit widely applicable relative permittivity values and affordable loss and are thus promising candidates for ultra-low sintering temperature applications.